|Product Test Report:||SGS,DVGW,AWWA,PETROCHINA||FACTORY REPORT:||TUV,BV|
butyl rubber sealing tape,
butyl rubber sealant tape
0.635mm black color 100width high strength polyethylene butyl rubber tape for corrosion protection of gas pipeline
The XUNDA-T-100 series is Cold applied tape coating system for corrosion protection of Oil, Gas, Petrochemical, and Waste Water underground or overhead pipelines.
The butyl rubber tape shall be applied after the Liquid adhesive and before the outer-layer tape by hand or with a wrapping machine
The specification of the tape consists of two layers, adhesive layer and film backing
Adhesive: Butyl rubber
Film backing: Special blend of stabilized polyethylene
Excellent adhesion to pipe and self
Can be applied over a wide temperature range
Good conformability and consistent uniform thickness
Easily applied with no special equipment
Compatible with common pipe coatings
Excellent resistance to cathodic disbonding
Meets ASTM D 1000 Standard
Ⅳ Physical Properties
Polythene Butyl tape (inner layer)
Elongation at Break³
Peel Adhesion to Primed Pipe
0.24 in radius 6.4 mm
2.5 x 1012 ohm.m
Water Vapor Transmission Rate £
ASTM F 1249
Water Absorption Rate
Recommended Application Temperature
Max Serve Temperature
-40 to 80℃
Available Roll Size (width x length)
2" to 32" X 50’ to 800’
Cold applied coating tape Application Instruction
1.Steel pipe pretreatment
1.1 Keeping the pipe external surface clean and dry. Remove the dust,
oil, welding slag, burrs, grease and dirt on pipe surface.
1.2 Pipe surface prepared up-to a level of Sa 2 or 2 ½ or St 2/st by sand blasting.
1.3 After the pre-cleaning operations, the pipe surface not smooth
which may sharp the pipe coating should be burnished , the abrasive
dust attached on the pipe surface should also be cleaned clearly.
1.4 If flash rusting occurs, the surfaces must be re-cleaned by blasting as above.
2.Coating &Wrapping application
2.1 Coating &wrapping application consist of primer application, inner
tape coating ,outer tape coating .
2.2 weather condition
2.2.1 When the wind&sand was strongly, when the sand and dust covered
on the surface of pipe, primer ,tape etc., should not be brushing primer
and wrapping the tape if there is no reliable preventive measures.
2.2.2 When air humidity is greater than 80%,or when the pipe surface is wet from any precipitation, should not be brushing primer and wrapping tape.
3.1 The brushing time should be control within 6 hours between the pipe surface treatment and brush primer. During brush primer, pipe surface should be free from damp and pollution. If the pipe surface rust return, should be re-pre-cleaned.
3.2 The primer should be mixed evenly in the container before brushing.
3.3 The primer should be applied uniformly, without any sags, floods, runs, drips, bare spot and over spray, such as leakage brush, clot, streaming. The primer coat DFT shall not be less than 25-50micron (1-2mils)
3.4 After the primer dried, then wrapping the tape(It usually takes 3to 5 minutes.).
machine application approx. 0,1 litre/m²
hand application approx. 0,2 litre/m²
4.Wrap tape application
4.1 Wrap tape application consists of hand application and machine application.
4.2 The tape applied temperature must be above 5 degrees,the coating construction temperature shall be more than -5 degrees as better .
4.3 The tape shall be spirally applied ,minimum overlap shall not be less than 50%.
4.4 When a new roll of tape started ,the ends shall be located to ensure the continuity of wrap tape using the same method of application.
4.5 Outer tape applied method is the same as above.
Cutbacks shall be a minimum 6inches(150mm) from the ends of each
pipe.The cutbacks may be tapered or straight edge for the total thickness
of the coating.
l Xunda Groups:
Jining Xunda Pipe Coating Materials CO.,Ltd
Shandong Xunda Science & Technology CO.,Ltd
Shandong Xunda Anticorrosion Heat-Shirnkable Technology CO.,Ltd
We are the most largest manufacturers of Polyethylene Tape for the Corrosion Control of pipelines and specialty applications. A joint-stock enterprise, possessing a gross investment of RMB 42 million, registered capital of RMB 10 million.
l A Global company supplying Polyethylene Coating Systems to the corrosion industry within the oil, gas and water pipeline construction industry for both onshore and offshore applications.
l A manufacturer of standard and specialty products.
l High-quality anti-corrosion systems providing anti-corrosion solutions for oil pipelines, natural gas, chemicals and water transmission and distribution pipelines, etc.
l Global supplier of PE corrosion system for metallic pipelines